PP S2040 SECCO SHANGHAI

365

Unit Price:US$ 1,016 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
82MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜high strength｜High temperature resistance
Application Areas:Fiber grade｜Non-woven fabric｜chip｜TV casing
Color:--
Grade:High melting point

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result
fisheye	0.8mm		合格品｜≤16 个/1520cm2
	fisheye	0.8mm		一等品｜≤8 个/1520cm2
		fisheye	0.8mm		优等品｜≤4 个/1520cm2
			fisheye	0.4mm		合格品｜≤60 个/1520cm2
				fisheye	0.4mm		一等品｜≤40 个/1520cm2
				fisheye	fisheye	0.4mm		优等品｜≤20 个/1520cm2
Cleanliness	色粒		合格品｜≤20 粒/kg树脂
Cleanliness	Cleanliness	色粒		一等品｜≤10 粒/kg树脂
Huangdu Index		ASTM D-192563T	2 %
Cleanliness	杂质		优等品｜≤20 粒/kg树脂
	Cleanliness	杂质		一等品｜≤40 粒/kg树脂
	Cleanliness	Cleanliness	杂质		合格品｜≤60 粒/kg树脂
Huangdu Index			优等品｜实测 %
	Huangdu Index			一等品｜实测 %
	Huangdu Index	Huangdu Index			合格品｜实测 %
Cleanliness	色粒		优等品｜≤5 粒/kg树脂

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D-1238	38.0 g/10min
density		ASTM D-1505	0.905 g/cm³
melt mass-flow rate			优等品｜32.0-43.0 g/10min
	melt mass-flow rate			一等品｜32.0-43.0 g/10min
	melt mass-flow rate	melt mass-flow rate			合格品｜30.0-38.0 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23℃		合格品｜≥10.0 kJ/m²
Bending modulus			优等品｜实测 GPa
elongation	Break	ASTM D-638	20 %
Rockwell hardness		ASTM D-785	94 R-Scale
tensile strength	Yield	ASTM D-638	34.0 Mpa
Impact strength of cantilever beam gap	23℃	ASTM D-256	16 J/m
Bending modulus		ASTM D-790A	1450 Mpa
Elongation at Break		ASTM D638/ISO 527	20 %
Bending modulus		ASTM D790/ISO 178	1450 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	94
tensile strength		ASTM D638/ISO 527	34 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	20 %
Bending modulus			一等品｜实测 GPa
Bending modulus	Bending modulus			合格品｜实测 GPa
elongation	Break		优等品｜≥20 %
	elongation	Break		一等品｜≥18 %
	elongation	elongation	Break		合格品｜≥18 %
tensile strength	Yield		优等品｜≥34.0 Mpa
	tensile strength	Yield		一等品｜≥31.0 Mpa
	tensile strength	tensile strength	Yield		合格品｜≥30.0 Mpa
Impact strength of cantilever beam gap	23℃		一等品｜≥10.0 kJ/m²
Rockwell hardness			优等品｜实测 R
	Rockwell hardness			一等品｜实测 R
	Rockwell hardness	Rockwell hardness			合格品｜实测 R
Impact strength of cantilever beam gap	23℃		优等品｜≥13.5 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.46MPa	ASTM D-648	99 °C
	Hot deformation temperature	HDT	ASTM D648/ISO 75	99 ℃（℉）
		Hot deformation temperature	0.45MPa		优等品｜实测 °C
			Hot deformation temperature	0.45MPa		一等品｜实测 °C
			Hot deformation temperature	Hot deformation temperature	0.45MPa		合格品｜实测 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238/ISO 1133	38.0 g/10min
density		ASTM D792/ISO 1183	0.905

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PP S2040 SECCO SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet