LCP

LCP E130I-VF2201 CELANESE USA

230

Unit Price:US$ 8,375 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive components｜Laptop case｜Electronic and Electrical Applications｜SMT application｜Terminal block｜Home appliance applications｜Lighting applications｜CPU socket｜Card slot
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	31 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	43 kJ/m²

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	45 %
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	13500 Mpa
bending strength	23°C	ISO 178	220 Mpa
Compressive modulus		ISO 604	14000 Mpa
Fracture bending strain		ISO 178	2.2 %
CompressiveStress	1%Strain	ISO 604	93.0 Mpa
Tensile modulus		ISO 527-2/1A/1	15000 Mpa
tensile strength	Break	ISO 527-2/1A/5	150 Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.6 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-06 cm/cm/°C
Melting temperature		ISO 11357-3	335 °C
Vicat softening temperature		ISO 306/B50	195 °C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	216 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	276 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.10 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.030 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V
Arc resistance		Internal Method	140 sec
Dissipation factor	2.05GHz	Internal Method	6E-03
	Dissipation factor	1MHz	IEC 60250	0.025
	Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.010
Relative permittivity	2.05GHz	Internal Method	4.23
	Relative permittivity	1MHz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	100Hz	IEC 60250	4.00
Dielectric strength		IEC 60243-1	32 KV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+14 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ISO 2039-2	71

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP E130I-VF2201 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet