POM HOSTAFORM® S 9244 CELANESE USA
201
- Unit Price:US$ 9,351 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜antioxidant｜Hydrolysis resistance
- Application Areas:Bottle cap｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 68.0 °C |
| melting temperature | ISO 11357-3 | 166 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C,局部断裂 | ISO 179/1eU | 200 kJ/m² |
| 23°C | ISO 179/1eU | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.40 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.6 % |
| MD | ISO 294-4 | 1.7 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 1.2 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.60 | |
| Dissipation Factor | 100Hz | IEC 60250 | 4E-03 |
| 1MHz | IEC 60250 | 6E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 1450 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 33.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 7.0 % |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | >50 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | 1200 Mpa |
| 1000hr | ISO 899-1 | 650 Mpa | |
| flexural modulus | 23°C | ISO 178 | 1450 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.