ABS TAIRILAC® AG15E1-H FCFC TAIWAN

556

Unit Price:US$ 1,376 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31.5MT
Delivery Terms:
FOB
Port of Loading :
Kaoshiung port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜High rigidity
Application Areas:Toy｜suitcase｜Phone｜calculator｜Clock housing｜Sound enclosure
Color:--
Grade:--

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	23°C	ASTM D638	52.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	52.0	Mpa
Bending modulus	23°C	ASTM D790	2750	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2750	Mpa
bending strength	23°C	ASTM D790	85.3	Mpa
bending strength	bending strength	23°C	ISO 178	86.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	84.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ISO 75-2/A	84.0	°C
		Hot deformation temperature	1.8MPa,Annealed	ASTM D648	94.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	94.0	°C
Vicat softening temperature		ASTM D15253	103	°C
Vicat softening temperature	Vicat softening temperature		ISO 306/A	103	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.8	g/10min
	melt mass-flow rate	220°C/10.0kg	ASTM D1238	20	g/10min
		melt mass-flow rate	200°C/5.0kg	ISO 1133	1.8	g/10min
		melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	20	g/10min
Shrinkage rate	MD	Internal Method	0.40-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	110
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ISO 2039-2	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.