Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	65 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	750 °C
Extreme Oxygen Index		ISO 4589-2	21 %

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178/A	10300 Mpa
bending strength	23°C	ASTM D790	207 Mpa
bending strength	bending strength	23°C	ISO 178	230 Mpa
Bending strain	23°C		3.0 %
Tensile modulus	23°C	ASTM D638	9980 Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2/1	10400 Mpa
tensile strength	Break,23°C	ASTM D638	123 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/5	145 Mpa
elongation	Break,23°C	ASTM D638	2.5 %
Tensile strain	Break,23°C	ISO 527-2/5	2.8 %
Tensile creep modulus	1hr	ISO 899-1	10000 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	8500 Mpa
Bending modulus	23°C	ASTM D790	8550 Mpa

thermal performance	Test Condition	Test Method	Test Result
TemperatureIndex	介电强度	IEC 60216	155
	TemperatureIndex	拉伸冲击强度	IEC 60216	140
	TemperatureIndex	TemperatureIndex	抗张强度	IEC 60216	155
Melting temperature		ISO 11357-3	225to250 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.27 W/m/K
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	125 °C
RTI Str		UL 746	140 °C
Half Interval	--8	IEC 60216	13.5 °C
	Half Interval	--9	IEC 60216	10.2 °C
	Half Interval	Half Interval	--10	IEC 60216	10.2 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Vicat softening temperature		ISO 306/B120	205 °C
Ball Pressure Test	220°C	IEC 60695-10-2	Pass

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.80 g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	30.0 cm3/10min
Shrinkage rate	TD:270°C,2.00mm2	ISO 294-4	0.90 %
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.20 %
		Shrinkage rate	MD:270°C,2.00mm2	ISO 294-4	0.30 %
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.10 %
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %
Viscosity value	降低的粘度	ISO 1628	91.0 ml/g

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	23°C,1.00mm	IEC 60243-1	27 KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.80
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	200 Mpa

film	Test Condition	Test Method	Test Result
Thin film puncture strength		ISO 6603-2	2.10 J
Thin film puncture strength	Thin film puncture strength		ISO 6603-2	650 N

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion		IEC 60426	A1
ISO Shortcut		ISO 7792	PBT+PET.GHLMR.09-100.GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Pocan® T7331 LANXESS GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet