HIPS POLYREX® PH-88 ZHENJIANG CHIMEI

687

Unit Price:US$ 1,730 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53.1MT
Delivery Terms:
FOB
Port of Loading :
Lianyungang port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜heat-resisting
Application Areas:Lighting fixtures｜Household goods｜Electronic field｜Electrical field
Color:--
Grade:Impact resistant grade

Material Certification

SGS

MSDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0	kJ/m²
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	11	kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	83	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	98	J/m
Charpy Notched Impact Strength	23°C	ISO 179	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	6.5	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--6	ISO 178	37.0	Mpa
bending strength	bending strength	--5	ASTM D790	37.2	Mpa
Bending modulus	--6	ISO 178	2100	Mpa
Bending modulus	Bending modulus	--5	ASTM D790	1930	Mpa
elongation	Break	ISO 527-2/50	40	%
elongation	elongation	Break4	ASTM D638	40	%
tensile strength	Break	ISO 527-2/50	24.0	Mpa
	tensile strength	Break4	ASTM D638	23.5	Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/50	26.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	80.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	74.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4.0E-5到6.0E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	90.0	°C
	Vicat softening temperature	--	ISO 306/A50	96.0	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15257	98.0	°C
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	94.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	89.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.40-0.70	%
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	5.50	cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	6.0	g/10min
density	23°C	ISO 1183	1.03	g/cm³
density	density	--3	ASTM D792	1.05	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L-Sale	ASTM D785	60

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Huaxiang	US$ 1290 /MT
Dongguan Yushifa	US$ 2080 /MT
Shenzhen Charter Gloy	US$ 2090 /MT
Shenzhen Qiyuda	US$ 2090 /MT

Supplier Join

Get App

Top

HIPS POLYREX® PH-88 ZHENJIANG CHIMEI

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index