PET Rynite®  FR515 BK DUPONT SHENZHEN

204
  • Unit Price:US$ 4,166 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardantenhanceFiller: Glass fiber reinforced material15% filler by weight
  • Application Areas:Electrical enclosureElectronic fieldElectrical field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU35 kJ/m²
Impact strength of simply supported beam without notch-40°CISO 179/1eU20 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.9mmUL 94V-0
Burning rate1.00mmISO 3795<100 mm/min
UL flame retardant rating1.5mmUL 945VA
UL flame retardant rating0.9mmIEC 60695-11-10,-20V-0
UL flame retardant rating1.5mmIEC 60695-11-10,-205VA
Extreme Oxygen IndexISO 4589-232 %
FMVSS flammabilityFMVSS302B
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthISO 178170 Mpa
Tensile modulusISO 527-26800 Mpa
tensile strengthBreakISO 527-2107 Mpa
Tensile strainBreakISO 527-22.6 %
Bending modulusISO 1785940 Mpa
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTD:55to160°CISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionTD:-40to23°CISO 11359-27E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:--ISO 11359-28.8E-05 cm/cm/°C
Linear coefficient of thermal expansionMD:55to160°CISO 11359-21.2E-05 cm/cm/°C
Linear coefficient of thermal expansionMD:-40to23°CISO 11359-23.3E-05 cm/cm/°C
Linear coefficient of thermal expansionMD:--ISO 11359-21.8E-05 cm/cm/°C
Melting temperatureISO 11357-3254 °C
Vicat softening temperatureISO 306/B50210 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A200 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B240 °C
Physical propertiesTest ConditionTest MethodTest Result
Top out temperature170 °C
Melt Volume Flow Rate (MVR)280°C/2.16kgISO 11336.00 cm3/10min
Shrinkage rateTD2ISO 294-41.2 %
Shrinkage rateTDISO 294-40.80 %
Shrinkage rateMDISO 294-40.30 %
Shrinkage rateMD2ISO 294-40.50 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931E+13 ohms
Compared to the anti leakage trace indexIEC 60112PLC 3
Compared to the anti leakage trace indexCTIUL 746PLC 3
Dissipation factor1MHzIEC 602500.015
Dissipation factor100HzIEC 602509E-03
Relative permittivity1MHzIEC 602503.50
Relative permittivity100HzIEC 602503.80
Dielectric strengthIEC 60243-134 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleISO 2039-288
Rockwell hardnessR-SaleISO 2039-2120
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.