PC IUPILON™  GS2010MDR GY MITSUBISHI ENGINEERING JAPAN

198
  • Unit Price:US$ 2,445 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhanceFiller: Glass fiber reinforced material10% filler by weight
  • Application Areas:Fiber gradeCamera applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 17955 kJ/m²
machinabilityTest ConditionTest MethodTest Result
Dry conditions热风干燥 120℃---約4-8小时
Processing temperature270-290 °C
Processing temperature290-310 °C
Processing temperature280-300 °C
Screw speed50-100 rpm
Mold temperature80-120 °C
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthISO 178135 Mpa
Bending modulusISO 1784000 Mpa
Tensile strainBreakISO 527-22.9 %
tensile strengthBreakISO 527-278.0 Mpa
Tensile modulusISO 527-24500 Mpa
bending strengthASTM D790/ISO 178107 kg/cm²(MPa)[Lb/in²]
Bending modulusASTM D790/ISO 1782900 kg/cm²(MPa)[Lb/in²]
Tensile modulusASTM D638/ISO 5273500 kg/cm²(MPa)[Lb/in²]
Elongation at BreakASTM D638/ISO 5274.8 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTDISO 11359-26.7E-05 cm/cm/°C
Linear coefficient of thermal expansionMDISO 11359-24E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A140 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B145 °C
Linear coefficient of thermal expansionASTM D696/ISO 113595.0E-05 mm/mm.℃
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateASTM D9550.3 - 0.5 %
densityASTM D792/ISO 11831.27
Water absorption rateSaturation,23°CISO 620.14 %
Shrinkage rateMD:3.20mm0.30-0.50 %
Shrinkage rateTD:3.20mm0.40-0.60 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min
melt mass-flow rate300°C/1.2kgISO 113310 g/10min
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexCTIUL 746PLC 4
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.