Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
60 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
80 kJ/m²
flammability
Test Condition
Test Method
Test Result
Atomization
G-value (condensate)
ISO 6452
3.0E-4 g
Atomization
F-value (refraction)
ISO 6452
95 %
FMVSS combustion rate
FMVSS 302
SE/B
Extreme Oxygen Index
ISO 4589-2
24 %
UL flame retardant rating
UL 94
HB
UL flame retardant rating
UL 94
HB
Burning rate
1.00 mm
ISO 3795
24 mm/min
mechanical properties
Test Condition
Test Method
Test Result
Tensile modulus
ISO 527-2
9800 Mpa
tensile strength
Break
ISO 527-2
195 Mpa
Tensile strain
Break
ISO 527-2
3.5 %
injection
Test Condition
Test Method
Test Result
drying temperature
80 °C
Drying time - hot air dryer
2.0 to 4.0 hr
Suggested maximum moisture content
0.20 %
Processing (melt) temperature
285 to 305 °C
Melt Temperature, Optimum
295 °C
Mold temperature
70 to 120 °C
Mold Temperature, Optimum
100 °C
Maintain pressure
50.0 to 100 Mpa
Maintain pressure
Drying Recommended
yes
Hold Pressure Time
3.00 s/mm
Maximum Screw Tangential Speed
12 m/min
thermal performance
Test Condition
Test Method
Test Result
Effective thermal diffusivity coefficient
6.85E-8 m²/s
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
9.5E-5 cm/cm/°C
Linear coefficient of thermal expansion
Flow
ISO 11359-2
2.8E-5 cm/cm/°C
Melting temperature
ISO 11357-3
262 °C
Glass transition temperature
ISO 11357-2
80.0 °C
Hot deformation temperature
1.8 MPa, Unannealed
ISO 75-2/A
253 °C
Hot deformation temperature
0.45 MPa, Unannealed
ISO 75-2/B
260 °C
Physical properties
Test Condition
Test Method
Test Result
Shrinkage rate
横向Flow
ISO 294-4
1.1 %
Shrinkage rate
Flow
ISO 294-4
0.30 %
Water absorption rate
Saturation, 23°C, 2.00 mm
ISO 62
6.9 %
Water absorption rate
Equilibrium, 23°C, 2.00 mm, 50% RH
ISO 62
2.0 %
Electrical performance
Test Condition
Test Method
Test Result
Compared to the anti leakage trace index
IEC 60112
V
Compared to the anti leakage trace index
3.00 mm
UL 746
PLC 0
Dissipation factor
1 MHz
IEC 62631-2-1
0.016
Dissipation factor
100 Hz
IEC 62631-2-1
0.016
Volume resistivity
IEC 62631-3-1
1.0E+11 ohms·m
Surface resistivity
IEC 62631-3-2
-- ohms
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)