PA66

PA66 TORZEN® G3300 L INVISTA USA

216

Unit Price:US$ 3,217 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜33% filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	285 Mpa
Bending modulus		ISO 178	9500 Mpa
Tensile strain	Break	ISO 527-2	3.1 %
tensile strength	Break	ISO 527-2	205 Mpa
Tensile modulus		ISO 527-2	10500 Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	12 kJ/m²
Charpy Notched Impact Strength	23℃	ISO 179	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-40℃	ISO 179	10 kJ/m²
bending strength		ISO 178	285 Mpa
Bending modulus		ISO 178	9500 Mpa
Elongation at Break		ISO 527	3.1 %
tensile strength	Break	ISO 527	205 Mpa
Tensile modulus		ISO 527	10500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	255 °C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	248 °C
Melting temperature	10℃/min	ISO 11357	262 °C
Hot deformation temperature	1.82 MPa, Unannealed	ISO 75	248 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75	255 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:2.00mm	ISO 294-4	0.90-1.1 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.30-0.40 %
Water absorption rate	23°C,24hr	ISO 62	1.2 %
	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.8 %
		Water absorption rate	Equilibrium, 23℃, 50% RH	ISO 62	1.8 %
		Water absorption rate	Water absorption rate	23℃, 24 hr	ISO 62	1.2 %
Shrinkage rate	平行: 2.00 mm	ISO 294-4	0.30- 0.40 %
Shrinkage rate	Shrinkage rate	正常: 2.00 mm	ISO 294-4	0.90 - 1.10 %
Fiberglass content		ISO 3451/4	33 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 TORZEN® G3300 L INVISTA USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet