PA6 Zytel® 73G50HSLA BK416 DUPONT USA
203
- Unit Price:US$ 1,017 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High gloss｜lubrication｜Good appearance
- Application Areas:Electronic and Electrical Applications｜Wear resistant accessories｜household electrical appliances
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.60 % | |
| MediumDensity | 1.24 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2050 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| Shrinkage rate | ISO 294-4 | 0.30 % | |
| Water absorption rate | ISO 62 | 4.5 % | |
| ISO 62 | 1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | 31 mm/min | |
| Flammability level | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15500 Mpa | |
| tensile strength | ISO 527-2 | 233 Mpa | |
| Tensile strain | ISO 527-2 | 2.2 % | |
| Tensile creep modulus | ISO 899-1 | -- Mpa | |
| ISO 899-1 | -- Mpa | ||
| Flexural modulus | ISO 178 | 14300 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 100 kJ/m² | |
| ISO 179/1eU | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Surface Resistivity | IEC 60093 | -- ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 219 °C | |
| ISO 75-2/A | 212 °C | ||
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 219 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.5E-05 cm/cm/°C | |
| ISO 11359-2 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.