Material Properties:crystallization｜High mobility｜Fast forming cycle｜Oil resistant
Application Areas:Thin walled components｜parts｜Shell
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.13 g/cm³
Melt volume flow rate		ISO 1133	175 cm3/10min
Water absorption rate		ISO 62	9.5 %
Water absorption rate	Water absorption rate		ISO 62	3.0 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	4.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	200 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179	250 kJ/m²
Impact strength of cantilever beam gap		ISO 180	3.0 kJ/m²
Charpy Notched Impact Strength		ISO 179	3.0 kJ/m²

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	3400 Mpa
tensile strength	ISO 527-2	88.0 Mpa
Tensile strain	ISO 527-2	3.8 %
Nominal tensile fracture strain	ISO 527-2	10 %
Flexural modulus	ISO 178	2900 Mpa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	65.0 °C
melting temperature		ISO 3146	220 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.