PC/PBT XENOY™  5220U-7A1D383 SABIC INNOVATIVE SHANGHAI

261
  • Unit Price:US$ 2,827 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    43MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Non enhanced｜Low temperature impact resistance｜Chemical resistance
  • Application Areas:--
  • Color:--
  • Grade:Flame retardant grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/1eA55 kJ/m²
Impact strength of cantilever beam gap-40°CASTM D256300 J/m
Impact strength of cantilever beam gap-30°CASTM D256530 J/m
Impact strength of cantilever beam gap23°CASTM D256710 J/m
Impact strength of cantilever beam gap-30°CISO 180/1A30 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A50 kJ/m²
Dart impact23°C,TotalEnergyASTM D376360.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainYieldASTM D6384.0 %
tensile strengthBreakISO 527-2/5050.0 Mpa
tensile strengthBreakASTM D63851.0 Mpa
tensile strengthYieldISO 527-2/5050.0 Mpa
tensile strengthYieldASTM D63853.0 Mpa
Tensile modulusISO 527-2/12050 Mpa
Tensile modulus--4ASTM D6382250 Mpa
Tensile modulus--3ASTM D6382250 Mpa
Tensile strainYieldISO 527-2/504.0 %
Tensile strainBreakASTM D638120 %
Tensile strainBreakISO 527-2/50120 %
Bending modulus50.0mmSpanASTM D7902030 Mpa
Bending modulusISO 1782000 Mpa
bending strengthISO 17880.0 Mpa
bending strengthYield,50.0mmSpanASTM D79084.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
RTI ImpUL 74675.0 °C
RTI StrUL 74675.0 °C
RTI ElecUL 74675.0 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-29E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8319E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-29.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CASTME8319.5E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B120125 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648107 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64884.0 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D64899.0 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af75.0 °C
Vicat softening temperatureASTM D152512122 °C
Vicat softening temperature--ISO 306/B50120 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateSaturation,23°CISO 620.50 %
Shrinkage rateTD2Internal Method0.80-1.0 %
Shrinkage rateMD：3.20mmInternal Method0.80-1.0 %
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113315.0 cm3/10min
melt mass-flow rate250°C/5.0kgISO 113316 g/10min
densityISO 11831.22 g/cm³
Specific volumeASTM D7920.830 cm³/g
densityASTM D7921.21 g/cm³
Outdoor applicabilityUL 746Cf2
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Electrical performanceTest ConditionTest MethodTest Result
Arc resistanceASTM D495PLC 5
Compared to the anti leakage trace indexCTIUL 746PLC 1
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.