PC Makrolon® 6487 013540 COVESTRO SHANGHAI
197
- Unit Price:US$ 3,398 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Good demolding performance｜Medium viscosity｜Flame retardant｜High impact resistance｜UV curing｜Processability
- Application Areas:Electrical field｜Electronic field｜Automotive sector｜Household appliances｜Household appliances｜Architectural application field｜Barrel｜Medical Supplies｜disposable
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 117 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/B | 134 °C | |
| RTI Elec | UL 746 | 125 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| vicat | ISO 306/B50 | 143 °C | |
| ISO 306/B120 | 141 °C | ||
| RTI Imp | UL 746 | 115 °C | |
| RTI Str | UL 746 | 125 °C | |
| Heat Deflection Temperature | ISO 75-2/A | 122 °C | |
| Glass Transition Temperature | ISO 11357-2 | 141 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlashIgnitionTemperature | ASTM D1929 | 470 °C | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C | |
| ApplicationofFlamefromSmallBurner-Method | DIN 53438-1,-3 | K1.F1 | |
| Burning rate - US-FMVSS | ISO 3795 | passed | |
| Hot filament ignition temperature | IEC 60695-2-13 | 930 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 36 % | |
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | IEC 60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 6000 N | |
| ISO 6603-2 | 5200 N | ||
| Charpy Notched Impact Strength | ISO 7391 | 12 kJ/m² | |
| ISO 7391 | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 7391 | 12 kJ/m² | |
| ISO 7391 | 65 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 55.0 J | |
| ISO 6603-2 | 50.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| relative permittivity | IEC 60250 | 3.10 | |
| IEC 60250 | 3.00 | ||
| Dissipation Factor | IEC 60250 | 8E-04 | |
| volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.12 % | ||
| shrinkage rate | ISO 2577 | 0.60-0.80 % | |
| ISO 2577 | 0.60-0.80 % | ||
| ISO 294-4 | 0.75 % | ||
| ISO 294-4 | 0.70 % | ||
| Apparent density | ISO 60 | 0.64 g/cm³ | |
| density | ISO 1183 | 1.20 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 10 g/10min | |
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2450 Mpa | |
| Bending Strain | ISO 178 | 7.0 % | |
| bending strength | ISO 178 | 75.0 Mpa | |
| ISO 178 | 99.0 Mpa | ||
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| flexural modulus | ISO 178 | 2450 Mpa | |
| Tensile strain | ISO 527-2/50 | 6.0 % | |
| ISO 527-2/50 | 120 % | ||
| tensile strength | ISO 527-2/50 | 66.0 Mpa | |
| ISO 527-2/50 | 65.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App