PC PANLITE® LV-2250Y TEIJIN JAPAN

188

Unit Price:US$ 3,212 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
48.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent
Application Areas:Electrical field｜Electronic field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Melt volume flow rate		ISO 1133	8.00 cm3/10min
Shrinkage rate		内部方法	0.50-0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.50-0.70 %
Water absorption rate		ISO 62	0.20 %

optical performance	Test Condition	Test Method	Test Result
transmittance		ASTM D1003/ISO 13468	88 %
refractive index		ASTM D542/ISO 489	1.585
refractive index	refractive index		ASTM D542	1.585
transmissivity		ASTM D1003	88.0 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-2
	UL flame retardant rating		UL 94	V-2
	UL flame retardant rating	UL flame retardant rating		UL 94	V-2
Burning wire flammability index		IEC 60695-2-12	875 °C
Burning wire flammability index	Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature		IEC 60695-2-13	875 °C

Mechanical properties	Test Method	Test Result
Tensile modulus	ASTM D638/ISO 527	2400 kg/cm²(MPa)[Lb/in²]
tensile strength	ASTM D638/ISO 527	61 kg/cm²(MPa)[Lb/in²]
elongation	ASTM D638/ISO 527	6 %
Flexural modulus	ASTM D790/ISO 178	2300 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	91 kg/cm²(MPa)[Lb/in²]
Flexural modulus	ISO 178	2300 Mpa
bending strength	ISO 178	91.0 Mpa
Tensile modulus	ISO 527-2/1	2400 Mpa
tensile strength	ISO 527-2/50	61.0 Mpa
Tensile strain	ISO 527-2/50	6.0 %
Nominal tensile fracture strain	ISO 527-2/50	>50 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
dielectric constant		ASTM D150/IEC 60250	3.1
dielectric constant	dielectric constant		ASTM D150/IEC 60250	3
Surface Resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric strength		IEC 60243-1	30 KV/mm
relative permittivity		IEC 60250	3.10
relative permittivity	relative permittivity		IEC 60250	3.00
Dissipation Factor		IEC 60250	1E-03
Dissipation Factor	Dissipation Factor		IEC 60250	9E-03
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 2

Physical properties	Test Method	Test Result
density	ASTM D792/ISO 1183	1200
Shrinkage rate	ASTM D955	0.5-0.7 %
Water absorption rate	ASTM D570/ISO 62	0.2 %

Thermal performance	Test Condition	Test Method	Test Result
vicat		ASTM D1525/ISO R306	149 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7 mm/mm.℃
Heat distortion temperature		ISO 75-2/B	142 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	129 °C
vicat		ISO 306/B50	149 °C
Linear coefficient of thermal expansion		ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	7E-05 cm/cm/°C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	115 °C
RTI Str		UL 746	125 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.