PA6

PA6 Zytel® 73G45L DUPONT USA

264

Unit Price:US$ 3,761 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Filler: Glass fiber reinforced material｜45% filler by weight
Application Areas:Electronic and electrical components｜Automotive Applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	18 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	120 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	120 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	19 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	44 mm/min
FMVSS flammability		FMVSS302	B
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	14500 Mpa
tensile strength	Break	ISO 527-2	230 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
Bending modulus		ISO 178	13000 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	-- Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.6E-05 cm/cm/°C
Melting temperature		ISO 11357-3	221 °C
Vicat softening temperature		ISO 306/B50	215 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	213 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	221 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.5 %
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	4.9 %
Shrinkage rate	MD	ISO 294-4	0.10 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.90 %
density		ISO 1183	1.51 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.