PPO/PA

PPO/PA NORYL GTX™ GTX979-74709 SABIC INNOVATIVE US

362

Unit Price:US$ 5,237 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
90MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜dimensional stability ｜High temperature resistance｜Hydrolysis resistance
Application Areas:Electrical applications｜Industrial machinery｜Application in the automotive field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	50.0 J

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	3.2mm	IEC 60695-2-12	650 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break4	ASTM D638	50.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	50.0 Mpa
elongation	Yield4	ASTM D638	5.0 %
	elongation	Yield	ISO 527-2/50	4.0 %
		elongation	Break4	ASTM D638	60 %
		elongation	elongation	Break	ISO 527-2/50	30 %
Bending modulus	50.0mmSpan5	ASTM D790	2050 Mpa
Bending modulus	Bending modulus	--6	ISO 178	2150 Mpa
bending strength	--6,7	ISO 178	80.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	80.0 Mpa
Tensile modulus	--3	ASTM D638	2000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2100 Mpa
tensile strength	Yield4	ASTM D638	55.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	55.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan10	ISO 75-2/Be	178 °C
Vicat softening temperature	--	ASTMD152511	180 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	182 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	9.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	9.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	9.6E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	185 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	280°C/5.0kg	ASTM D1238	15 g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	11.0 cm3/10min
Shrinkage rate	MD:3.20mm	Internal Method	1.2-1.6 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	1.2-1.6 %
Water absorption rate	Saturation,23°C	ISO 62	4.2 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		Internal Method	1.0E+3-1.0E+4 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX979-74709 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet