Material Description

Material Properties:Flame retardant｜Glass fiber reinforced
Application Areas:Fitness equipment｜Automotive sector｜Electrical field｜Electronic field｜Electrical appliances
Color:--
Grade:Wear resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C	ISO 179/1eU	50	kJ/m²
	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
UL flame retardant rating	UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2	2.6	%
tensile strength	Break	ISO 527-2	170	Mpa
Tensile modulus		ISO 527-2	10200	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Mold Temperature, Optimum			100	°C
Mold temperature			70 to 120	°C
Melt Temperature, Optimum			290	°C
Processing (melt) temperature			280 to 300	°C
Suggested maximum moisture content			0.20	%
Drying time - hot air dryer			2.0 to 4.0	hr
drying temperature			80	°C
Maximum Screw Tangential Speed			12	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	262	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	240	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24 hr, 23°C, 2.00 mm	ISO 62	0.60	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 2
Dielectric strength	2.00 mm	IEC 60243-1	24	KV/mm
Volume resistivity		IEC 62631-3-1	> 1.0E+13	ohms·m
Surface resistivity		IEC 62631-3-2	--	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.