Material Properties:Flame retardant grade｜Glass fiber reinforced｜Low Specific Gravity｜Stable forming size｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Electronic and electrical components｜lighting
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	105 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.8E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VB

Physical properties	Test Condition	Test Method	Test Result
Melt volume flow rate	300°C/2.16kg	ISO 1133	24.0 cm3/10min
shrinkage rate	TD:3.20mm		0.30-0.50 %
shrinkage rate	shrinkage rate	MD:3.20mm		0.20-0.40 %
Water absorption rate	饱和,23°C	ISO 62	0.060 %

Electrical performance	Test Method	Test Result
Surface Resistivity	IEC 60093	1E+15 ohms
volume resistivity	IEC 60093	5E+15 ohms·cm
Compared to the Leakage Tracking Index (CTI)	IEC 60112	V

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	6100 Mpa
tensile strength	断裂,23°C	ISO 527-2	75.0 Mpa
Tensile strain	断裂,23°C	ISO 527-2	2.7 %
flexural modulus	23°C	ISO 178	6000 Mpa
bending strength	23°C	ISO 178	122 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.