TPE Hytrel® 4069 DUPONT USA
332
- Unit Price:US$ 12,163 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:19MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Aging resistance｜Low temperature resistance｜High temperature resistance
- Application Areas:Electrical appliances｜Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:Extrusion grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.11 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 8.5 g/10min | |
| Melt volume flow rate | ISO 1133 | 8.80 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| ISO 294-4 | 0.80 % | ||
| Water absorption rate | ISO 62 | 0.70 % | |
| ISO 62 | 0.70 % | ||
| ISO 62 | 0.30 % | ||
| MediumDensity | 1.10 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 37 | |
| ISO 868 | 33 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | <100 mm/min | |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| IEC 60695-11-10,-20 | HB | ||
| IEC 60695-11-10,-20 | HB | ||
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor | VDA270 | 4.00 | |
| Emissions of Organic Compounds | VDA277 | 10.0 µgC/g |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | NoBreak | |
| ISO 179/1eA | NoBreak | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180/1A | NoBreak | |
| ISO 180/1A | NoBreak | ||
| Charpy Notched Impact Strength | ISO 179/1eA | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 3.20 Mpa | |
| ISO 527-2 | 6.70 Mpa | ||
| Tensile strain | ISO 527-2 | >300 % | |
| Nominal tensile fracture strain | ISO 527-2 | 800 % | |
| Flexural modulus | ISO 178 | 45.0 Mpa | |
| Tensile modulus | ISO 527-2 | 45.0 Mpa | |
| tensile strength | ISO 527-2 | 29.0 Mpa |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ISO 34-1 | 100 kN/m | |
| ISO 34-1 | 100 kN/m |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water Vapor Transmission Rate | DIS15106-1/-2 | 900 g/m²/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 0.013 | |
| IEC 60250 | 0.020 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | IEC 60250 | 4.80 | |
| IEC 60250 | 4.70 | ||
| dielectric strength | IEC 60243-1 | 18 KV/mm | |
| Volume resistivity | IEC 60093 | 4E+12 ohms·cm | |
| Surface Resistivity | IEC 60093 | 3E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ISO 974 | -96.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | -50.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.8E-04 cm/cm/°C | |
| ISO 11359-2 | 2E-04 cm/cm/°C | ||
| ISO 11359-2 | 2.8E-04 cm/cm/°C | ||
| ISO 11359-2 | 2.2E-04 cm/cm/°C | ||
| melting temperature | ISO 11357-3 | 193 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.