LCP

LCP SUMIKASUPER® E6007LHF-MR-Z SUMITOMO JAPAN

361

Unit Price:US$ 4,557 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
105MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage｜Good forming performance｜Glass fiber reinforced｜enhance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	250 J/m

flammability	Test Condition	Test Method	Test Result
Solder resistance		Internal Method	300 °C
Extreme Oxygen Index		ISO 527-1	40 %
UL flame retardant rating	0.30 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ASTM D790	158 Mpa
Bending modulus	23°C	ASTM D790	11800 Mpa
elongation	Break	ASTM D638	5.1 %
tensile strength		ASTM D638	157 Mpa

injection	Test Condition	Test Method	Test Result
Temperature at the rear of the barrel			280 to 320 °C
drying time			4.0 to 24 hr
drying temperature			130 °C
Back pressure			1.00 to 5.00 Mpa
Screw speed			50 to 100 rpm
Temperature in the middle of the barrel			320 to 340 °C
Temperature at the front of the material cylinder			340 to 360 °C
Spray nozzle temperature			340 to 360 °C
Processing (melt) temperature			350 °C
Mold temperature			40 to 160 °C
Injection pressure			80.0 to 160 Mpa
Injection speed			中等偏快
Maintain pressure			20.0 to 40.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	8.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 150°C	Internal Method	2.0E-6 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	269 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation	ASTM D570	0.020 %
Shrinkage rate	Flow	Internal Method	0.20 %
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	0.60 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 3
Arc resistance		ASTM D495	124 sec
Dissipation factor	1.00 GHz	ASTM D150	4.0E-3
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.026
Dielectric constant	1.00 GHz	ASTM D150	3.50
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.80
Volume resistivity		ASTM D257	1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	106

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP SUMIKASUPER® E6007LHF-MR-Z SUMITOMO JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet