Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜50% filler by weight
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Method	Test Result
melt mass-flow rate	g/10min	3.6to20
Flow: 23 ℃	mm/mm	38.1E-3-78.7E-3
Melt volume flow rate	ISO 527-2/5	0.01to0.04
Balance, 23 ℃, 50% RH	%	0.70to1.5
23℃,24hr	%	0.16to0.30
Saturation, 23 ℃	%	0.060to0.15

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		°C	798to904

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		J/m	0.222to0.332
Impact strength of simply supported beam without notch		kJ/m²	2.647to20.893

Mechanical properties	Test Method	Test Result
Fracture, 23 ℃		151.72to280.69 MPa
Yield, 23 ℃	%	2.0to3.0
Fracture, 23 ℃	%	1.6to2.1

Electrical performance	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	V
dielectric strength	V/mil	500to840
Surface Resistivity	ohms	5.0E+3-6.0E+15
Volume resistivity	ohms·cm	3.0E+2-2.1E+16

Thermal performance	Test Method	Test Result
horizontal	mm/mm/°C	55.9E-5-50.8E-5
0.45MPa, Not annealed	°C	234to255
1.8MPa, Not annealed	°C	223to230
flow	mm/mm/°C	137.2E-5-25.4E-5

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.