PPA AMODEL® A-4133L BK324 SOLVAY USA

360

Unit Price:US$ 5,907 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
63MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low moisture absorption｜Filler: Glass fiber reinforced material｜33% filler by weight
Application Areas:Shell｜Vehicle electronics｜currency｜Lawn and garden equipment｜Laptop case｜Industrial components｜Valves/valve components｜Metal substitution｜Industrial applications｜Thick wall accessories (components)｜Phone｜Application in the automotive field｜Machine/mechanical components｜Electrical/Electronic Applications｜Parts under the hood of a car
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	1070nm:1.60mm	ASTM D1003	>20 %
transmissivity	transmissivity	940nm:1.60mm	ASTM D1003	>20 %

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	59 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	67 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	11700 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.6 %
	Tensile strain	Break,24°C	ISO 527-2	4.3 %
		Tensile strain	Break,150°C	ISO 527-2	6.6 %
		Tensile strain	Tensile strain	Break,175°C	ISO 527-2	6.6 %
Bending modulus		ASTM D790	11000 Mpa
Tensile modulus	23°C	ISO 527-2	12600 Mpa
	Tensile modulus	100°C	ISO 527-2	6830 Mpa
		Tensile modulus	150°C	ISO 527-2	5310 Mpa
		Tensile modulus	Tensile modulus	175°C	ISO 527-2	4830 Mpa
tensile strength		ASTM D638	200 Mpa
	tensile strength	Break,23°C	ISO 527-2	211 Mpa
		tensile strength	Break,24°C	ISO 527-2	125 Mpa
			tensile strength	Break,150°C	ISO 527-2	87.6 Mpa
			tensile strength	tensile strength	Break,175°C	ISO 527-2	79.3 Mpa
elongation	Break	ASTM D638	2.5 %
Bending modulus	23°C	ISO 178	10400 Mpa
	Bending modulus	100°C	ISO 178	7170 Mpa
		Bending modulus	150°C	ISO 178	4620 Mpa
		Bending modulus	Bending modulus	175°C	ISO 178	4210 Mpa
bending strength		ASTM D790	290 Mpa
	bending strength	23°C	ISO 178	296 Mpa
		bending strength	100°C	ISO 178	177 Mpa
			bending strength	150°C	ISO 178	111 Mpa
			bending strength	bending strength	175°C	ISO 178	99.3 Mpa
compressive strength		ASTM D695	179 Mpa
shear strength		ASTM D732	89.6 Mpa
Poisson's ratio			7.58 0.41

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed,3.20mm	ASTM D648	320 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	294 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTM D648	300 °C
Continuous use temperature		ASTM D3045	210 °C
Melting temperature		ISO 11357-3	327 °C
Melting temperature	Melting temperature		ASTM D570	327 °C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	7.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.2E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ASTM D955	0.50 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.0 %
Water absorption rate	24hr	ASTM D570	0.29 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	2E+16 ohms·cm
Dielectric strength	1.60mm	ASTM D149	20 KV/mm
Dielectric constant	60Hz	ASTM D150	3.80
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.60
Dissipation factor	60Hz	ASTM D150	4E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.012
Compared to the anti leakage trace index	CTI	UL 746	V
High voltage arc tracing rate	HVTR	UL 746	mm/min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA AMODEL® A-4133L BK324 SOLVAY USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet