PA66

PA66 Zytel® 70G43L BK031 DUPONT USA

282

Unit Price:US$ 3,960 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
60MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜high strength
Application Areas:Electrical field｜Electronic field｜Fitness equipment
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt density			1.29 g/cm³
Top out temperature			210 °C
Specific Heat Capacity of Melt			2050 J/kg/°C
Thermal Conductivity of Melt			0.25 W/m/K

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	110 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	110 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00 mm	ISO 3795	27 mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ISO 4589-2	23 %
FMVSS combustion rate		FMVSS 302	B

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	340 Mpa
Bending modulus		ISO 178	12000 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1 hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	225 Mpa
Tensile modulus		ISO 527-2	14000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Mold temperature			70 to 120 °C
Mold Temperature, Optimum			100 °C
Processing (melt) temperature			285 to 305 °C
Melt Temperature, Optimum			295 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	2.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	9.0E-6 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C
Vicat softening temperature		ISO 306/B50	255 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	255 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	7.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	6.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.3E-4 cm/cm/°C
Effective thermal diffusivity coefficient			9.50E-8 m²/s

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5 %
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.7 %
	Water absorption rate	Water absorption rate	24 hr, 23°C, 2.00 mm	ISO 62	0.90 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.0 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 62631-3-2	-- ohms
Volume resistivity		IEC 62631-3-1	> 1.0E+13 ohms·m
Dielectric strength		IEC 60243-1	27 KV/mm
Relative permittivity	1 MHz	IEC 62631-2-1	4.10
Relative permittivity	Relative permittivity	100 Hz	IEC 62631-2-1	4.50
Dissipation factor	100 Hz	IEC 62631-2-1	0.010
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.015

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	125
Rockwell hardness	Rockwell hardness	M -Sale	ISO 2039-2	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top