PEI

PEI ULTEM™ STM1700-7101 SABIC INNOVATIVE US

223

Unit Price:US$ 22,818 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	V-0
Extreme Oxygen Index		ASTM D2863	48 %

elastomer	Test Condition	Test Method	Test Result
tear strength	1.60mm	ISO 34-1	37 kN/m

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2/50	59.0 Mpa
elongation	Yield	ASTM D638	5.0 %
Tensile strain	Yield	ISO 527-2/50	5.0 %
elongation	Break	ASTM D638	20 %
Tensile strain	Break	ISO 527-2/50	15 %
Bending modulus	--	ASTM D790	2150 Mpa
	Bending modulus	50.0mmSpan4	ASTM D790	2150 Mpa
	Bending modulus	Bending modulus		ISO 178	2000 Mpa
bending strength		ASTM D790	94.0 Mpa
	bending strength		ISO 178	98.0 Mpa
	bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	94.0 Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	50.0 mg
Tensile modulus		ASTM D638	2400 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2300 Mpa
tensile strength	Yield	ASTM D638	62.0 Mpa
	tensile strength	Yield	ISO 527-2/50	68.0 Mpa
	tensile strength	tensile strength	Break	ASTM D638	53.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	164 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	145 °C
Glass transition temperature		DSC	200 °C
Vicat softening temperature		ISO 306/B120	180 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	295°C/6.6kg	ASTM D1238	7.0 g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.87-0.92 %
Water absorption rate	Saturation,23°C	ISO 62	0.76 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	ASTM D150	5.4E-03
Surface resistivity		ASTM D257	>1.0E+15 ohms
Volume resistivity		ASTM D257	>1.0E+16 ohms·cm
Dielectric strength	3.20mm,inOil	ASTM D149	17 KV/mm
Dielectric constant	100Hz	ASTM D150	3.13
	Dielectric constant	100kHz	ASTM D150	3.07
	Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.04
Dissipation factor	100Hz	ASTM D150	0.011
Dissipation factor	Dissipation factor	100kHz	ASTM D150	6.1E-03

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ASTM D2240	80

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ STM1700-7101 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet