Material Properties:Very high stiffness and thickness reduction capability｜Good optical properties｜High temperature resistance｜Enhance the barrier performance of water vapor｜High creep resistance｜Good elasticity and thermal strength｜The application of shrink film can improve the shrinkage force and enhance the burn through resistance
Application Areas:Suitable for simple or composite blown film applications｜in compliance with｜Outer packaging bag｜Laundry bag｜Shrinking film (mixed in small amounts)｜Containing 10-30% LLDPE and steaming bag
Color:--
Grade:Injection grade

Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
characteristic			耐高温
purpose			热水壶、取暖器、咖啡壶等家用电器

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	HDT	ASTM D648/ISO 75	140 ℃（℉）
melting temperature			8 ℃（℉）
vicat		ASTM D1525/ISO R306	156 ℃（℉）

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ASTM D256/ISO 179	4 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	8 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	8 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	4 kg·cm/cm(J/M)ft·lb/in
Elongation at break		ASTM D638/ISO 527	100 %
Tensile modulus		ASTM D638/ISO 527	120 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	430 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	130
flexural modulus		ASTM D790/ISO 178	24000 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	430 kg/cm²(MPa)[Lb/in²]

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.