'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
TPEE RITEFLEX® 672 CELANESE USA
302
- Unit Price:US$ 2,800 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity
- Application Areas:Automotive components｜High temperature hot plugging adhesive
- Color:--
- Grade:--
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak | |
| -30°C | ISO 179/1eU | NoBreak | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| elastomer | Test Condition | Test Method | Test Result | Test Unit |
| tear strength | ASTM D624 | 214 | kN/m | |
| Flow | ISO 34-1 | 190 | kN/m | |
| Permanent compression deformation | 23°C | ASTM D395 | <1.0 | % |
| Shore hardness | -- | Internal Method | 40 | % |
| -- | ASTM D2632 | 40 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | -40°C | ISO 178 | 2400 | Mpa |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | >50 | % | |
| elongation | Break,23°C | ASTM D638 | 300 | % |
| Tensile strain | Yield | ISO 527-2/1A/50 | 19 | % |
| tensile strength | 50%Strain | ISO 527-2 | 25.0 | Mpa |
| 10%Strain | ISO 527-2 | 27.0 | Mpa | |
| 5.0%Strain | ISO 527-2 | 21.0 | Mpa | |
| Break | ISO 527-2 | 40.0 | Mpa | |
| Break,23°C | ASTM D638 | 29.2 | Mpa | |
| Yield | ISO 527-2/1A/50 | 28.0 | Mpa | |
| Tensile modulus | 23°C | ASTM D638 | 635 | Mpa |
| ISO 527-2/1A/1 | 500 | Mpa | ||
| Bending modulus | 23°C | ISO 178 | 450 | Mpa |
| bending strength | 23°C | ISO 178 | 22.0 | Mpa |
| Taber wear resistance | 1000Cycles,CS-18Wheel | ASTM D4060 | 30.0 | mg |
| RossFlex | Internal Method | >1.0E+6 | cycles | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Glass transition temperature | ASTM D3418 | -23.3 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 118 | °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.4E-04 | cm/cm/°C |
| MD | ASTM D696 | 1.7E-04 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 215 | °C | |
| ASTM D3418 | 214 | °C | ||
| Vicat softening temperature | ASTM D1525 | 204 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.802 | cm³/g | |
| melt mass-flow rate | ASTM D1238 | 10to15 | g/10min | |
| ISO 1133 | 16 | g/10min | ||
| Shrinkage rate | MD | ASTM D955 | 2.0 | % |
| TD | ISO 294-4 | 1.7-2.2 | % | |
| MD | ISO 294-4 | 1.7-2.2 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 0.040 | |
| Relative permittivity | 1MHz | IEC 60250 | 3.70 | |
| Dielectric strength | IEC 60243-1 | 28 | KV/mm | |
| Surface resistivity | IEC 60093 | 2E+17 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | ShoreD,15Sec | ISO 868 | 72 | |
| ShoreD | ASTM D2240 | 72 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| tear strength | Kg/m | 217.2 | kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.