PPS

PPS LATILUB K/30 LATI ITALY

207

Unit Price:US$ 5,219 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Carbon fiber reinforced material｜30% filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	280 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	270 °C
Continuous use temperature			225 °C
Vicat softening temperature		ISO 306/B50	255 °C
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	2E-06 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:2.00mm	ISO 294-4	0.15-0.25 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.10-0.20 %
Water absorption rate	23°C,24hr	ISO 62	0.050 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1E+02 ohms
Volume resistivity		ASTM D257	1E+04 ohms·cm

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	25000 Mpa
	Tensile modulus	60°C	ISO 527-2/1	23500 Mpa
		Tensile modulus	90°C	ISO 527-2/1	21000 Mpa
			Tensile modulus	120°C	ISO 527-2/1	15000 Mpa
			Tensile modulus	Tensile modulus	150°C	ISO 527-2/1	11000 Mpa
tensile strength	Break,23°C	ISO 527-2/5	185 Mpa
	tensile strength	Break,60°C	ISO 527-2/5	165 Mpa
		tensile strength	Break,90°C	ISO 527-2/5	130 Mpa
			tensile strength	Break,120°C	ISO 527-2/5	85.0 Mpa
			tensile strength	tensile strength	Break,150°C	ISO 527-2/5	70.0 Mpa
Tensile strain	Break,23°C	ISO 527-2/5	0.80 %
	Tensile strain	Break,60°C	ISO 527-2/5	0.90 %
		Tensile strain	Break,90°C	ISO 527-2/5	1.3 %
			Tensile strain	Break,120°C	ISO 527-2/5	1.6 %
			Tensile strain	Tensile strain	Break,150°C	ISO 527-2/5	1.8 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	25 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPS LATILUB K/30 LATI ITALY

Material Description

Technical Data Sheet Compare

Technical Data Sheet