PC LEXAN™ 3412HF SABIC INNOVATIVE US

257

Unit Price:US$ 2,933 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
52.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜High rigidity｜Flame retardant｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Electrical applications｜Automotive Applications｜electrical equipment
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	110	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	530	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	3.39	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-1
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ASTM D638	107	Mpa
elongation	Break	ASTM D638	4.0	%
Bending modulus	50.0mmSpan	ASTM D790	5520	Mpa
tensile strength	Yield	ASTM D638	100	Mpa
Tensile modulus		ASTM D638	3450	Mpa
bending strength	Break,50.0mmSpan	ASTM D790	165	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	157	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	142	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	138	°C
RTI Str		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	80.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.34	g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	8.5	g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.40	%
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.45-0.65	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.