PC LEXAN™ PK2870-21317 SABIC INNOVATIVE US

297

Unit Price:US$ 2,318 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜wear resistant
Application Areas:chip｜Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Transmittance rate	2.54 mm	ASTM D1003	88 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	V-notch Edgew，-30℃	ISO 179/1eA	50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	V-notch Edgew，23℃	ISO 179/1eA	70 kJ/m²
Impact strength of cantilever beam gap	/，30℃	ASTM D256	150 J/m
Suspended wall beam without notch impact strength	80103，-30℃	ISO 180/1A	55 kJ/m²
Impact strength of cantilever beam gap	23℃	ASTM D256	750 J/m
Suspended wall beam without notch impact strength	80103，23℃	ISO 180/1A	75 kJ/m²
	Suspended wall beam without notch impact strength	23℃	ASTM D 4812	NB J/m
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	80103，23℃	ISO 180/1U	NB kJ/m²
Dart impact		ASTM D 3029	170 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Type I, 5，Yield	ASTM D638	62 Mpa
	tensile strength	50 mm/m，Yield	ISO 527	65 Mpa
		tensile strength	50 mm/m，Break	ISO 527	70 Mpa
		tensile strength	tensile strength	Type I, 50，Break	ASTM D638	65 Mpa
elongation	Type I, 5，Yield	ASTM D638	7 %
elongation	elongation	50 mm/m，Yield	ISO 527	7 %
Elongation at Break	Type I, 5	ASTM D638	70 %
Elongation at Break	Elongation at Break	50 mm/m	ISO 527	70 %
bending strength	1.3 mm/min/，Yield	ASTM D790	95 Mpa
bending strength	bending strength	2 mm/，Yield	ISO 178	95 Mpa
Bending modulus	2 mm/mi	ISO 178	2300 Mpa
Bending modulus	Bending modulus	1.3 mm/min	ASTM D790	2300 Mpa

thermal properties	Test Condition	Test Method	Test Result
Vicat softening temperature	Rate B/5	ASTM D1525	150 °C
	Vicat softening temperature	Rate B/5	ISO 306	150 °C
	Vicat softening temperature	Vicat softening temperature	Rate B/5	ISO 306	149 °C
specific heat		ASTM C 351	1.25 J/g-°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	2 cm³/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/2.16 kg	ISO 1133	4 cm³/10 min
melt mass-flow rate	/	ASTM D1238	2.5 g/10min
Shrinkage rate	flow, 3.	Internal	0.5-0.7
Water absorption rate	equilibriu	ASTM D570	0.58
	Water absorption rate	equilibriu	ASTM D570	0.35
		Water absorption rate	23°C/sat	ISO 62	0.35
		Water absorption rate	Water absorption rate	23°C / 50	ISO 62	0.15

hardness	Test Condition	Test Method	Test Result
Hardness (Rockwell R)		ISO 2039-2	120 R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ PK2870-21317 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet