Material Properties:High transparency｜Moderate heat resistance｜High adhesion｜High mobility
Application Areas:Electrical field｜Electronic field｜film｜sheet｜Kitchen utensils｜Wood parts｜Imitation｜Food containers
Color:--
Grade:High liquidity level

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
combustibility	1/8"	UL 94	HB
vicat	1000g	ASTM D-1525	98 °C
combustibility	1/8"	IEC 707	FH3-28 mm/min
Heat Deflection Temperature	Unannealed 18.5kg/cm	ASTM D-648	82 °C
combustibility	1/16"	UL 94	HB
melt mass-flow rate	220℃/5Kg	ASTM D-1238	9 g/10min

Other performance	Test Method	Test Result
High Voltage Arc Traceability Rate (HVTR)	UL 746A	PLC 0
High arc combustion index (HAI)	UL 746A	PLC 0
Hot wire ignition (HWI)	UL 746A	PLC 5
arc resistance	ASTM D-495	PLC_5
Compared to the Leakage Tracking Index (CTI)	UL 746A	PLC 5

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate		ASTM D-955	0.4-0.8 %
density		ASTM D-792	1.05

mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness	R-scale	ASTM D-785	119
bending strength	15mm/min	ASTM D-790	850 kg/cm
tensile strength	50mm/min	ASTM D638	450 kg/cm
Impact strength of cantilever beam gap	Notched 1/8"	ASTM D-256	1.5 kg.cm/cm
elongation	50mm/min	ASTM D-638	4 %
flexural modulus	15mm/min	ASTM D-790	32000 kg/cm
Impact strength of cantilever beam gap	Notched 1/4"	ASTM D-256	1.1 kg.cm/cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.