POM S731 TORAY JAPAN

334

Unit Price:US$ 3,070 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
POM TENAC™-C 7520 ASAHI JAPAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:High liquidity level

Material Certification

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.22	%
melt mass-flow rate	190℃	ASTM D-1238	27	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D-790	2.70	GPa
Impact strength of cantilever beam gap		ASTM D-1822	100	KJ/m
bending strength		ASTM D790/ISO 178	94	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2.70	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	82
tensile strength		ASTM D638/ISO 527	64	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	50	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	55	kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D-785	M82（R115）
shear strength		ASTM D-732	56	Mpa
tensile strength		ASTM D-638	64	Mpa
Impact strength of cantilever beam gap	有切口	ASTM D-256	55	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	无切口	ASTM D-256	640	J/m
Dielectric strength	3mmt	ASTM D-149	19	MV/m
elongation	Break	ASTM D-638	50	%
bending strength		ASTM D-790	94	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.82MPa	ASTM D-648	110	°C
Melting temperature		DSC	166	°C
Hot deformation temperature	0.45MPa	ASTM D-648	158	°C
flammability		UL 94	HB
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	10	mm/mm.℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	158	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	110	℃（℉）
Linear coefficient of thermal expansion		ASTM D-696	10
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570/ISO 62	0.22	%
melt mass-flow rate		ASTM D1238/ISO 1133	27	g/10min
density		ASTM D792/ISO 1183	1.41
Shrinkage rate	垂直	东丽法	1.8	%
Shrinkage rate	Shrinkage rate	Across Flow	东丽法	1.9	%
Friction coefficient	相对钢材	ASTM D-1894	0.15
Friction coefficient	Friction coefficient	同系Resin	ASTM D-1894	0.35
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	50Hz	ASTM D-150	0.005
Dielectric constant	50Hz	ASTM D-150	3.7
Compared to the Leakage Traceability Index (CTI)		IEC (CTI)	600	V
Dielectric constant	10	ASTM D-150	3.7
Arc resistance		ASTM D-495	＞200	sec
Volume resistivity	10	ASTM D-257	4
Dissipation factor	10	ASTM D-150	0.005

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

POM S731 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index