PC/PBT XENOY™ ENH2900-WH9GG37 SABIC INNOVATIVE SHANGHAI
280
- Unit Price:US$ 3,092 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:108MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Low temperature impact resistance
- Application Areas:Household daily necessities｜Electrical applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 78.0 °C |
| vicat | ASTM D15255 | 102 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-1 |
| 1.5 mm | UL 94 | V-0 | |
| 2.5 mm | UL 94 | 5VB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 266°C/5.0 kg | ASTM D1238 | 26 g/10 min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.80 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Suggested injection volume | 30 to 80 % | ||
| Temperature at the rear of the barrel | 220 to 255 °C | ||
| Temperature in the middle of the barrel | 220 to 265 °C | ||
| Temperature at the front of the material cylinder | 245 to 275 °C | ||
| Spray nozzle temperature | 245 to 275 °C | ||
| Processing (melt) temperature | 245 to 275 °C | ||
| mold temperature | 60 to 80 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.038 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2480 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 63.0 Mpa |
| 断裂 | ASTM D638 | 42.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| 断裂 | ASTM D638 | 65 % | |
| flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2240 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 89.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.