PC Makrolon® 6487-704609 COVESTRO SHANGHAI
193
- Unit Price:US$ 3,336 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Good demolding performance｜Medium viscosity｜Flame retardant｜High impact resistance｜UV curing｜Processability
- Application Areas:Electrical field｜Electronic field｜Automotive sector｜Household appliances｜Household appliances｜Architectural application field｜Barrel｜Medical Supplies｜disposable
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 117 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/B | 134 °C | |
| vicat | ISO 306/B50 | 143 °C | |
| ISO 306/B120 | 141 °C | ||
| Heat Deflection Temperature | ISO 75-2/A | 122 °C | |
| Glass Transition Temperature | ISO 11357-2 | 141 °C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| ISO 11359-2 | 6.5E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 125 °C | |
| RTI Str | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 115 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA | ||
| FlashIgnitionTemperature | ASTM D1929 | 470 °C | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 900 °C | |
| IEC 60695-2-13 | 930 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 36 % | |
| ApplicationofFlamefromSmallBurner-Method | DIN 53438-1,-3 | K1.F1 | |
| Burning rate - US-FMVSS | ISO 3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | IEC 60426 | A1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 66.0 Mpa | |
| ISO 527-2/50 | 65.0 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 2450 Mpa | |
| bending strength | ISO 178 | 75.0 Mpa | |
| ISO 178 | 99.0 Mpa | ||
| Bending Strain | ISO 178 | 7.0 % | |
| Tensile strain | ISO 527-2/50 | 6.0 % | |
| ISO 527-2/50 | 120 % | ||
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| flexural modulus | ISO 178 | 2450 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 7391 | 12 kJ/m² | |
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 5200 N | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 55.0 J | |
| ISO 6603-2 | 50.0 J | ||
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 6000 N | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | ISO 7391 | 12 kJ/m² | |
| ISO 7391 | 65 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 7391 | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.20 g/cm³ | |
| shrinkage rate | ISO 294-4 | 0.70 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.12 % | ||
| shrinkage rate | ISO 2577 | 0.60-0.80 % | |
| ISO 294-4 | 0.75 % | ||
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| shrinkage rate | ISO 2577 | 0.60-0.80 % | |
| Apparent density | ISO 60 | 0.64 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 10 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| IEC 60112 | V | ||
| relative permittivity | IEC 60250 | 3.10 | |
| IEC 60250 | 3.00 | ||
| Dissipation Factor | IEC 60250 | 8E-04 | |
| IEC 60250 | 9E-03 | ||
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | IEC 60093 | 1E+16 ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.