PC PANLITE® MN-3600HA QM00431HA TEIJIN JAPAN

Unit Price:US$ 2,431 /MT
Packaging Specification:
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜Flame retardant｜Good impact resistance｜Good liquidity｜Halogen-free
Application Areas:Electrical field｜Electronic field｜Automotive sector
Color:--
Grade:--

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.00 mm	UL 94	V-1	无
	UL flame retardant rating	1.50 mm	UL 94	V-0	无
	UL flame retardant rating	UL flame retardant rating	2.00 mm	UL 94	5VB	无
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃, 24 hr	ISO 62	0.22	%
Tensile modulus		ISO 527-2/1	2350	Mpa
tensile strength	Yield	ISO 527-2/50	60	Mpa
Elongation at Break		ISO 527-2/50	100	%
Elongation at Break	Elongation at Break		ISO 527-2/50	50	%
Bending modulus		ISO 178	2300	Mpa
bending strength		ISO 178	95	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ISO 527-2/5	50	Mpa
elongation at yield		ISO 527-2/50	7	%
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	125	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	112	°C
Linear coefficient of thermal expansion	Flow	ASTM D696	0.000070	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横动	ASTM D696	0.000070	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	280℃/2.16 kg	ISO 1133	17	g/10 min
Shrinkage rate	横向Flow : 4.00 mm	ISO 294-4	0.5-0.7	%
Shrinkage rate	Shrinkage rate	Flow : 4.00 mm	ISO 294-4	0.5-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1000000000000000	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.19	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.