Material Properties:Chemical resistance｜Low moisture absorption｜Filler: Glass fiber reinforced material｜33% filler by weight
Application Areas:Shell｜Vehicle electronics｜Phone｜Industrial components｜Automotive interior parts｜Industrial applications｜Metal substitution｜Fuel pipeline｜Machine/mechanical components｜Application in the automotive field｜Power/Other Tools｜Laptop case｜Parts under the hood of a car
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.80MPa退火	ISO 75-2/Af	280 °C
vicat	熔融温度	ISO 11357-3	313 °C

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.5mm
	UL flame retardant rating		UL -94	HB 3.0mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 0.84mm

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.48 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	1E+15 Ω.cm
dielectric strength	3.20mm	IEC 60243-1	39 KV/mm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	233 Mpa
Elongation at break	23°C	ISO 527-2	2.5 %
Tensile modulus	23°C	ISO 527-2	13400 Mpa
bending strength	23°C	ISO 178	319 Mpa
flexural modulus	23°C	ISO 178	11600 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	73 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.8 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.