ABS POLYLAC® PA-707K ZHENJIANG CHIMEI

Unit Price:US$ 2,050 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading :
Lianyungang port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS POLYLAC® PA-707 TAIWAN CHIMEI

Transaction Guarantee:

Supplier Information

Shenzhen Qiyuda Trading Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜High gloss
Application Areas:Office supplies｜Lighting fixtures｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

MSDS

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高光泽性高刚性
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃ 10kg	ISO 1133	23	g/10min
melt mass-flow rate	melt mass-flow rate	200℃ 5kg	ASTM D-1238	1.9	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D-790	860	kg/cm2
Impact strength of cantilever beam gap		ASTM D256/ISO 179	15(2.7)	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	860（12.200）	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	29000（41000）	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-116
elongation		ASTM D638/ISO 527	15	%
tensile strength		ASTM D638/ISO 527	500（7.090）	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	14(2.6)	kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D-790	2.9	104kg/cm2
Rockwell hardness		ASTM D-785	116	R
tensile strength		ASTM D-638	500	kg/cm2
Impact strength of cantilever beam gap	1/4〃(1/8")	ASTM D-256	14(15)	kg.cm/cm
Elongation at Break		ASTM D-638	15	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1/16"	File NO.E196075	HB
Hot deformation temperature	Annealed（Unannealed）	ASTM D-648	99(210)/88(190)	℃(°F)
Vicat softening temperature		ASTM D1525/ISO R306	105(221)	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	88(190)	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	99(210)	℃（℉）
Combustibility (rate)		UL 94	1/16"HB
Vicat softening temperature		ASTM D-1525	105(221)	℃(°F)
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	23	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	1.9	g/10min
density		ASTM D792/ISO 1183	1.06(1.9)

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 1780 /MT

Supplier Join

Get App

Top

ABS POLYLAC® PA-707K ZHENJIANG CHIMEI