PC LEXAN™ BFL2000 SABIC INNOVATIVE US

226

Unit Price:US$ 3,290 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Fuzzy coefficient (Haze)		ISO 14782	--	%
Transmittance rate		ASTM D1003/ISO 13468	--	%
Refractive index		ASTM D542/ISO 489	--
other	Test Condition	Test Method	Test Result	Test Unit
remarks			注射成型
characteristic			加阻燃剂.无卤.无溴.阻燃
Color			本色
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	1/8“5.7	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	--	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	1/8“5.2	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	缺口：11	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	--	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	--	%
Tensile modulus		ASTM D638/ISO 527	363000（361000）	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	8700（7250）	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	5.0	%
Rockwell hardness		ASTM D785	--
Bending modulus		ASTM D790/ISO 178	355000（344000）	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	13500（13100）	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	70	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-2-V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	--	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	280	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	280	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.000039	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.29
Shrinkage rate		ASTM D955	0.50-0.70	%
melt mass-flow rate		ASTM D1238/ISO 1133	300℃/1.2kg.32	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	--	g/10min
Water absorption rate		ASTM D570/ISO 62	0.15	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	>1.0E+15 ohms	Ω
Dielectric constant		ASTM D150/IEC 60250	50/60HZ.3.20
Dielectric constant	Dielectric constant		ASTM D150/IEC 60250	3.20
Arc resistance		ASTM D495/IEC 60112	--
Volume resistivity		ASTM D257/IEC 60093	1.0E+15 ohm cm	Ω.cm
Dielectric loss		ASTM D150/IEC 60250	50/60HZ.0.010
Dielectric loss	Dielectric loss		ASTM D150/IEC 60250	0.010

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.