PC/ABS

PC/ABS CYCOLOY™ CX7240-7T1A4544 SABIC INNOVATIVE NANSHA

213

Unit Price:US$ 3,028 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High impact resistance｜High mobility
Application Areas:Architectural application field｜Outdoor applications｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling｜Electrical field｜Electronic field｜Engine hood parts｜Medical supplies
Color:--
Grade:High liquidity level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.60 mm	UL 94	V-1
	UL flame retardant rating	0.75 mm	UL 94	V-0
		UL flame retardant rating	1.5 mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	0.75 mm13	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.75 mm13	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825 °C
		Hot filament ignition temperature	1.5 mm13	IEC 60695-2-13	775 °C
			Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C
			Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm13	IEC 60695-2-13	775 °C
Extreme Oxygen Index		ISO 4589-2	34 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2600 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600 Mpa
tensile strength	Yield3	ASTM D638	65.0 Mpa
	tensile strength	Yield	ISO 527-2/50	65.0 Mpa
		tensile strength	Break3	ASTM D638	58.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0 Mpa
elongation	Yield3	ASTM D638	4.1 %
	elongation	Yield	ISO 527-2/50	4.0 %
		elongation	Break3	ASTM D638	100 %
		elongation	elongation	Break	ISO 527-2/50	90 %
Bending modulus	50.0 mm Span4	ASTM D790	2500 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2500 Mpa
bending strength	--5,6	ISO 178	96.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	104 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			230 to 280 °C
Temperature in the middle of the barrel			240 to 290 °C
Temperature at the front of the material cylinder			250 to 300 °C
Spray nozzle temperature			250 to 300 °C
Processing (melt) temperature			250 to 300 °C
Mold temperature			60 to 85 °C
Exhaust hole depth			0.030 to 0.075 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	93.0 °C
Vicat softening temperature	--	ASTM D152511	110 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	113 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.20 W/m/K
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI		UL 746	90.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	18 g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35 KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25 KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17 KV/mm
Compared to the anti leakage trace index		UL 746	PLC 3
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ CX7240-7T1A4544 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet