Plastic Raw Materials
PC

PC LEXAN™  943A-116 SABIC INNOVATIVE SINGAPHORE

374
  • Unit Price:US$ 2,789 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Weather resistance｜Flame retardant｜transparent｜UV resistance｜Medium viscosity
  • Application Areas:Casters｜Household appliances｜Household appliances｜Automotive sector
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376350.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A50 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A70 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94V-0
UL flame retardant rating3.0mmUL 945VA
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldISO 527-2/5055.0 Mpa
tensile strengthBreakASTM D63860.0 Mpa
tensile strengthBreakISO 527-2/5060.0 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D638130 %
Tensile strainBreakISO 527-2/50130 %
Bending modulus50.0mmSpanASTM D7902060 Mpa
Bending modulusISO 1782200 Mpa
bending strengthISO 17885.0 Mpa
Tensile modulusASTM D6382100 Mpa
Tensile modulusISO 527-2/12100 Mpa
tensile strengthYieldASTM D63858.0 Mpa
bending strengthYield,50.0mmSpanASTM D79089.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648135 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648120 °C
Vicat softening temperatureASTM D15259140 °C
Vicat softening temperatureISO 306/B120140 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8316.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8316.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.7E-05 cm/cm/°C
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
RTI StrUL 746120 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strength3.20mm,inOilASTM D14917 KV/mm
Dielectric strength3.20mm,in OilIEC 60243-116 KV/mm
Dielectric constant50HzASTM D1502.95
Dielectric constant60HzASTM D1502.95
Dielectric constant1MHzASTM D1502.90
Dissipation factor50HzASTM D1502.4E-03
Dissipation factor60HzASTM D1502.4E-03
Dissipation factor1MHzASTM D1508.5E-03
Compared to the anti leakage trace indexCTIUL 746PLC 3
Compared to the anti leakage trace indexIEC 60112PLC 3
High arc combustion indexHAIUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.