POK

POK POKETONE™ M330F HYOSUNG KOREA

548

Unit Price:US$ 3,173 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
370MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance｜High chemical resistance｜High wear resistance｜High gas barrier｜High flame retardancy
Application Areas:automobile｜Electronic appliances｜Industrial materials
Color:--
Grade:--

Material Certification

TDS

MSDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23℃	ISO 6603-2	50 J
Impact strength of cantilever beam gap	-30℃	ISO 180/1A	3 kJ/m²
	Impact strength of cantilever beam gap	-30℃	ASTM D256	40 kJ/m²
		Impact strength of cantilever beam gap	-10℃	ISO 180/1A	4 kJ/m²
			Impact strength of cantilever beam gap	-10℃	ASTM D256	60 kJ/m²
				Impact strength of cantilever beam gap	23℃	ISO 180/1A	7 kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ASTM D256	95 kJ/m²
Suspended wall beam without notch impact strength		ASTM D256	N.B.

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	1400
Bending modulus	Bending modulus		ASTM D790	1500
bending strength		ASTM D790	57 Mpa
Elongation at Break		ASTM D638	300 %
elongation at yield		ASTM D638	21 %
Tensile modulus		ISO 527-1	1500 Mpa
Tensile modulus	Tensile modulus		ASTM D638	1600 Mpa
tensile strength	Yield	ASTM D638	60 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ASTM D955	222 °C
Linear coefficient of thermal expansion	25℃ to 55℃	ASTM E831	0.000097
Vicat softening temperature	5 kg	ASTM D-1525	195 °C
Vicat softening temperature	Vicat softening temperature	50 N	ISO 306/B50	190 °C
Hot deformation temperature	66psi	ASTM D648	200 °C
	Hot deformation temperature	264psi	ASTM D648	105 °C
		Hot deformation temperature	0.45 MPa	ISO 75	190 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa	ISO 75	92 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD, 2 mm	ASTM D955	1.6 %
	Shrinkage rate	TD, 2 mm	ASTM D955	1.5 %
		Shrinkage rate	TD, 3 mm	ASTM D955	2 %
		Shrinkage rate	Shrinkage rate	MD, 3 mm	ASTM D955	2 %
melt mass-flow rate	240℃，2.16kg	ISO 1133	56
melt mass-flow rate	melt mass-flow rate	240℃，2.16kg	ASTM D1238	60 g/10min
saturated		ASTM D570	2.1 %
Water absorption rate	Equilibrium，50%RH	ASTM D570	0.5 %
Rockwell hardness		ASTM D785	110
Shore hardness		ISO 868	77

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	短期，3 mm	ASTM D149	15 KV/mm
Dielectric strength	Dielectric strength	短期，2 mm	ASTM D149	19 KV/mm
Volume resistivity		ASTM D257	1000000000000000 ohms·cm
Surface resistivity		ASTM D257	1000000000000000000 ohm/sq
Arc resistance		ASTM D495	130 sec
Compared to the anti leakage trace index		IEC 112	V
Dielectric constant	60Hz	ASTM D150	6.2
Dielectric constant	Dielectric constant	60Hz	IEC 250	5
Dissipation factor	60Hz	ASTM D150	0.008
Dissipation factor	Dissipation factor	60Hz	IEC 250	0.013

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.