PA66 LNP™ KONDUIT™ PX10323 BKNAT SABIC INNOVATIVE US
78
- Unit Price:US$ 3,552 /MT
- Packaging Specification:
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Dimensional stability｜Low Specific Gravity
- Application Areas:Automotive body panels｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flow: -40 to 40 ° C | ASTME831 | 1.6E-05 cm/cm/°C | |
| Flow: -30 to 80 ° C | ISO 11359-2 | 1.4E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 3.6E-05 cm/cm/°C |
| Horizontal: -30 to 80 ° C | ISO 11359-2 | 4E-05 cm/cm/°C | |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 4.8E-05 cm/cm/°C |
| --11 | ASTM D790/ISO 178 | 3.5 W/m/K | |
| --12 | ASTM D790/ISO 178 | 15 W/m/K | |
| --13 | ISO 22007-2 | 1.5 W/m/K | |
| --14 | ISO 22007-2 | 18 W/m/K | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 186 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 200 °C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | Pass |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | HB |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 850650 °C |
| 1.60mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 825 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 26 J/m | |
| ISO 180/1A | 3.0 kJ/m² | ||
| ASTM D4812 | 150 J/m | ||
| ISO 180/1U | 8.0 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD:24小时 | ASTM D955 | 0.15 % |
| TD:24小时 | ASTM D955 | 0.17 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 3E+05 ohms |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 10800 Mpa | |
| fracture | ASTM D638 | 54.0 Mpa | |
| ISO 527-2/5 | 75.0 Mpa | ||
| ASTM D638 | 1.0 % | ||
| ISO 527-2/5 | 0.90 % | ||
| 50.0mm span | ASTM D790 | 12400 Mpa | |
| --5 | ISO 178 | 14000 Mpa | |
| --6 | ISO 178 | 90.0 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 78.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.