Material Description
- Material Properties:High heat resistance
- Application Areas:Automotive components｜Electronic and electrical components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 4.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.80 % | |
| 内部方法 | 0.50 - 0.80 % | ||
| Water absorption rate | ASTM D570 | 0.10 % | |
| ASTM D570 | 0.70 % | ||
| ASTM D570 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2090 Mpa | |
| tensile strength | ASTM D638 | 49.0 Mpa | |
| ISO 527-2/50 | 55.0 Mpa | ||
| ASTM D638 | 49.0 Mpa | ||
| ISO 527-2/50 | 40.0 Mpa | ||
| elongation | ASTM D638 | 5.0 % | |
| ISO 527-2/50 | 5.0 % | ||
| ASTM D638 | 110 % | ||
| ISO 527-2/50 | 70 % | ||
| Flexural modulus | ASTM D790 | 2090 Mpa | |
| ISO 178 | 2200 Mpa | ||
| bending strength | ISO 178 | 80.0 Mpa | |
| ASTM D790 | 94.0 Mpa | ||
| Poisson's ratio | ASTM E132 | 0.40 | |
| Taber abraser | ASTM D1044 | 16.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 35 kJ/m² | |
| ISO 179/1eA | 45 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| dielectric constant | ASTM D150 | 3.30 | |
| ASTM D150 | 3.30 | ||
| ASTM D150 | 3.10 | ||
| Dissipation Factor | ASTM D150 | 2.0E-3 | |
| ASTM D150 | 2.0E-3 | ||
| ASTM D150 | 0.020 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 50 to 80 % | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Spray nozzle temperature | 255 to 270 °C | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| Temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.013 to 0.020 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Be | 125 °C | |
| ISO 75-2/Ae | 105 °C | ||
| vicat | ISO 306/A50 | 140 °C | |
| ISO 306/B50 | 130 °C | ||
| ISO 306/B120 | 135 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 7.6E-5 cm/cm/°C | |
| ASTM D696 | 7.9E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.18 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.