PC LEXAN™ 3413R-739 SABIC INNOVATIVE JAPAN
288
- Unit Price:US$ 2,594 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 92 |
| R计秤 | ASTM D785 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| specific heat | ASTMC351 | 1130 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.22 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 151 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 146 °C | |
| vicat | ASTM D15255 | 165 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 2.2E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | V-1 | |
| 3.0mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C | ASTM D3029 | 5.00 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 67.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1.1E-03 |
| 60Hz | ASTM D150 | 1.1E-03 | |
| 1MHz | ASTM D150 | 7E-03 | |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 5 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.35 |
| 60Hz | ASTM D150 | 3.35 | |
| 1MHz | ASTM D150 | 3.31 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 5.0 g/10min |
| 300°C/5.0kg | ASTM D1238 | 19 g/10min | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.14 % |
| 平衡,23°C | ASTM D570 | 0.26 % | |
| Specific volume | ASTM D792 | 0.697 cm³/g |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D638 | 100 Mpa |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 6610 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 153 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 24.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.