PBT Cristin® T841FR DUPONT USA
181
- Unit Price:US$ 3,105 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:15.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact｜Filler: Glass fiber reinforced material｜10% filler by weight
- Application Areas:Home appliance accessories｜Wear resistant accessories｜Electronic and electrical accessories
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 170 °C |
| 8.0MPa,未退火 | ISO 75-2/C | 66.0 °C | |
| vicat | ISO 306/B50 | 180 °C | |
| melting temperature | ISO 11357-3 | 205 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 30 % | |
| FMVSS flammability | FMVSS302 | DNI |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
| 23°C | ISO 179/1eU | 46 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 27 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| 1MHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| 1MHz | IEC 60250 | 0.018 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 1.31 g/cm³ | ||
| melt viscosity | 250°C,1000sec^-1 | ISO 11443 | 240000 mPa·s |
| Ejection Temperature | 150 °C | ||
| SpecificHeatCapacity of Melt | 1970 J/kg/°C | ||
| ThermalConductivityofMelt | 0.23 W/m/K | ||
| shrinkage rate | TD | ISO 294-4 | 1.2 % |
| MD | ISO 294-4 | 0.70 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.35 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3900 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 70.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 4.7 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 3000 Mpa |
| 1000hr | ISO 899-1 | 2000 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App