other	Test Condition	Test Method	Test Result	Test Unit
characteristic			阻燃级
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C	kJ/m²	140
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm		V-0	--
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	（24hr）23°C	ASTM D-570	1.1	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	MPa	125	70.0
bending strength	bending strength	80°C	MPa	65.0	--
Taber abraser	1000Cycles	mg	9.00to10.0	--
bending strength	-40°C	MPa	170	--
Bending modulus	80°C	MPa	1200	--
Bending modulus	Bending modulus	23°C	MPa	3500	1500
Tensile strain	Break,23°C	%	7.5	7.5
tensile strength	80°C	MPa	45.0	--
tensile strength	tensile strength	23°C	MPa	85.0	65.0
Bending modulus	-40°C	ASTM D-790	34500	kg/cm
bending strength	-40°C	ASTM D-790	1210	kg/cm
Tensile and flexural strength	23°C	ASTM D-638	850	kg/cm
Ezo De Wei Sheng	Unnotched1/2" 23°C		5	kg.cm/cm
tensile strength	23°C，Break	ASTM D-638	12	kg/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		差示扫描测热计DSC法	265	°C
Hot deformation temperature	4.6kg/cm	ASTM D-648	244	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	°C	244	--
Melting temperature		°C	265	--
Melting temperature	Melting temperature			265	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	%	7.5	--
Water absorption rate	Water absorption rate	23°C,24hr	%	1.1	--
Shrinkage rate	MD：3.00mm4	%	1.0-1.6
Shrinkage rate	Shrinkage rate	MD：1.00mm3	%	0.60-0.90
Flame resistant grade		UL 94	113
density		ASTM D792/ISO 1183	1.18
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the Leakage Traceability Index (CTI)	导热率温度指表	UL 746	600	V
Volume resistivity		ASTM D-257	V-0	Ω.cm
Dielectric strength	1/8" 短时间	ASTM D-149	17	KV/mm
Arc resistance	1/8"	ASTM D-150	127
Volume resistivity		ohms·cm	1E+15	--
Dielectric strength		kV/mm	28	--
Dielectric constant	23°C,50Hz		5.20	--
Dissipation factor	23°C,50Hz		0.070	--
Arc resistance		sec	127	--
Compared to the anti leakage trace index	CTI	V	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C		120	--

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.