Material Properties:High rigidity｜High hardness｜Low contractility｜Low warpage｜Anti creep｜VOC
Application Areas:Automotive sector｜Industrial machinery｜Engine parts｜bearing｜machine｜Mechanical components
Color:--
Grade:Enhanced level

Technical Data Sheet

Basic performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ISO 1133	2.7	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ISO 179-1	6.6	kJ/㎡
tensile strength		ISO 527-1.2	133.4	Mpa
bending strength		ISO 178	183.8	Mpa
Charpy Notched Impact Strength		GB/T1043.1-2008	8.78	kJ/m²
Tensile stress	Yield	GB/T1040.1，2-2006	123.6	Mpa
Tensile modulus		GB/T1042.1，2-2006	9463	Mpa
Nominal fracture strain		GB/T1042.1，2-2006	10.32	%
bending strength		-------	185.9	Mpa
Fiberglass content		-------	24.92	Mpa
Shore hardness			79.9	hrm
Bending modulus			7554	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa	10-5cm/cm*℃	158.2	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa	-------	157.9	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ISO 2577	1.52	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.