PC/ABS CYCOLOY™ CX7240 7M1D106 SABIC INNOVATIVE NANSHA
199
- Unit Price:US$ 4,366 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:22MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High impact resistance｜High mobility
- Application Areas:Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 100 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 99.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10 | ISO 75-2/Af | 93.0 °C | |
| vicat | -- | ASTM D152511 | 110 °C |
| -- | ISO 306/B120 | 113 °C | |
| ball-indentation hardness | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 90.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 |
| 0.75 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | 5VB | |
| 3.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| 0.75 mm13 | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75 mm13 | IEC 60695-2-13 | 775 °C |
| 1.0 mm | IEC 60695-2-13 | 825 °C | |
| 1.5 mm13 | IEC 60695-2-13 | 775 °C | |
| 3.0 mm | IEC 60695-2-13 | 800 °C | |
| 3.0 mm13 | IEC 60695-2-13 | 775 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 34 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16 kg | ASTM D1238 | 18 g/10 min |
| Melt volume flow rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.60 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.20 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 230 to 280 °C | ||
| Temperature in the middle of the barrel | 240 to 290 °C | ||
| Temperature at the front of the material cylinder | 250 to 300 °C | ||
| Spray nozzle temperature | 250 to 300 °C | ||
| Processing (melt) temperature | 250 to 300 °C | ||
| mold temperature | 60 to 85 °C | ||
| Exhaust hole depth | 0.030 to 0.075 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2600 Mpa |
| -- | ISO 527-2/1 | 2600 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 65.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| 断裂3 | ASTM D638 | 58.0 Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 4.1 % |
| 屈服 | ISO 527-2/50 | 4.0 % | |
| 断裂3 | ASTM D638 | 100 % | |
| 断裂 | ISO 527-2/50 | 90 % | |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2500 Mpa |
| --5 | ISO 178 | 2500 Mpa | |
| bending strength | --5,6 | ISO 178 | 96.0 Mpa |
| 屈服, 50.0 mm 跨距4 | ASTM D790 | 104 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.