Material Properties:Moderate liquidity｜Fast forming cycle｜High impact resistance｜High rigidity
Application Areas:Electrical appliances｜Automotive sector｜Rigid package｜Seat｜Industrial applications｜Consumer goods sector｜Child safety seats｜Consumer product application field｜Application in the automotive field
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	52.0 °C
	Heat Deflection Temperature	0.45MPa,未退火	ASTM D648	100 °C
	Heat Deflection Temperature	Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/Bf	91.5 °C

Impact resistance	Test Condition	Test Method	Test Result
Dart impact	-29°C,3.18mm	ASTM D5420	22.8 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/2.16kg	ASTM D1238	8.0 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	1330 Mpa
tensile strength	屈服3	ASTM D638	25.9 Mpa
tensile strength	tensile strength	屈服	ISO 527-2/50	25.8 Mpa
elongation	屈服3	ASTM D638	5.2 %
elongation	elongation	屈服	ISO 527-2/50	4.0 %
flexural modulus	1%正割4	ASTM D542	1360 Mpa
	flexural modulus	1%正割5	ASTM D790B	1540 Mpa
	flexural modulus	flexural modulus	--6	ISO 178	1260 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.