Material Description
- Material Properties:Easy to demould｜Non halogenated
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 11 g/10 min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % | |
| Water absorption rate | ASTM D570 | 0.15 % | |
| ASTM D570 | 0.35 % | ||
| ASTM D570 | 0.58 % | ||
| Outdoor applicability | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 70 | |
| ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | ASTM D1003 | 88.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ASTM D2863 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 62.0 Mpa | |
| ASTM D638 | 65.0 Mpa | ||
| elongation | ASTM D638 | 7.0 % | |
| ASTM D638 | 110 % | ||
| Flexural modulus | ASTM D790 | 2340 Mpa | |
| bending strength | ASTM D790 | 93.0 Mpa | |
| Taber abraser | ASTM D1044 | 10.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 3200 J/m | |
| Dart impact | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| dielectric strength | ASTM D149 | 15 KV/mm | |
| dielectric constant | ASTM D150 | 3.17 | |
| ASTM D150 | 3.17 | ||
| ASTM D150 | 2.96 | ||
| Dissipation Factor | ASTM D150 | 9.0E-4 | |
| ASTM D150 | 9.0E-4 | ||
| ASTM D150 | 0.010 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Hot wire ignition (HWI) | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 137 °C | |
| ASTM D648 | 132 °C | ||
| vicat | ASTM D15255 | 154 °C | |
| Linear coefficient of thermal expansion | ASTM E831 | 6.8E-5 cm/cm/°C | |
| specific heat | ASTM C351 | 1250 J/kg/°C | |
| thermal conductivity | ASTM C177 | 0.19 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.